Water based acrylic semi gloss varnish

Water based acrylic semi gloss varnish
Rate : 1

Since solvent based varnish are harmful for human health and need too much environmental considerations, Water base varnish have gained lots of efforts for improvement. These varnish are significantly biocompatible and slightly toxic. While Water-base varnish vapor is lightly hazardous and doesn’t include ignition danger like it’s solvent based type, Water base acrylic varnish are recommended for use alongside Alvan Water base acrylic paint as topcoat for improving coatings durability in every condition like light resistance, weather resistance and helps development of a glossy smooth surface. Less drying time and a good-looking finish are also these varnish properties. Other advantages for this type of lacquer are wash ability, better strength in final coating, ease of application and miscibility with water, lacking of malodor, abrasion resistance, UV and light resistance and biocompatibility.Since solvent based lacquers are harmful for human health and need too much environmental considerations, waterborne lacquers have gained lots of efforts for improvement. These lacquers are significantly biocompatible and slightly toxic. While waterborne lacquer vapor is lightly hazardous and doesn’t include ignition danger like it’s solvent based type, waterborne acrylic lacquers are recommended for use alongside Alvan waterborne acrylic paint as topcoat for improving coatings durability in every condition like light resistance, weather resistance and helps development of a glossy smooth surface. Less drying time and a good-looking finish are also these lacquers properties. Other advantages for this type of lacquer are wash ability, better strength in final coating, ease of application and miscibility with water, lacking of malodor, abrasion resistance, UV and light resistance and biocompatibility
This product is specifically To create a semi-shiny surface used .to increase Water base acrylic paint’s resistance and lifetime in addition to better gloss under sunlight.
  • Appearance: liquid
  • Solid content by weight (%): 38
  • Solid content by volume (%): 35
  • Density (gr/cm3): 1.05
  • Wet film thickness (µ): 100
  • Dry film thickness (µ): 35
  • Theoretical spreading rate (m2/lit): 10
  • Touch dry (hr): 1
  • Dry trough time (hr): 3
  • Min interval time (hr): 3
  • Full cure (days): 1
Generally, a Opaque surface formed of rough created into it, and Opaque agents by creation this the rough on the surface, irregularities light reflection and leads to be seen a Opaqued surface. In the semi-gloss water-based acrylic varnish used from nanoparticles as Opaque agents.
According to the international standard, namely as “Paints and varnishes - Determination of gloss value at 20 degrees, 60 degrees, and 85 degrees” to number ISO 2813 and according to the method test mentioned in this standard means “Standard Test Method for Specular Gloss” to number ASTM D523 amount of glossiness this product evaluated which results that including the following table:
Glossiness ( in the 60-degree angle )
70GU>*>10GUStandard acceptable limit
126GUWitness sample
43.9GUNano sample



The evaluation of the "glossiness" of acrylic varnish demonstrated the amount of light reflected off the surface that the varnish had been applied to it. According to the standard, the amount of glossiness in the 60-degree angle must be between 10 to 70 GU for the semi-glossiness varnish. Clearly, the glossiness of Nano sample stayed on in the standard range while the witness sample possess very high the glossiness.
Shake product well before use. Mix it with sufficient amount of water and then apply on substrate. The amount of lacquer and water mixture for brush, rollers and pistol are 10-15, 5-10 and 20-25 %wt. respectively. It’s recommended to store it in over than 10 Celsius degrees, 3 Celsius degrees more than dew point and humidity less than %80. Keep it cool and dry and also avoid direct sun light. Expiry date is 30 months after production.
Keep the container cool and dry and also avoid direct sun light in good ventilation. Avoid freezing. Close tight after use. Best usage period in case of well storage is 30 months after production. If swallowed or in case of eye contact (wash with plenty of water then) seek medical attention immediately.

Product Standard

  • NanoScale Certification

    NanoScale Certification

    Standard Date : 2016/08/30

    Expire Date : 2017/08/31